Utjecaj kinematičkih faktora zavarivanja trenjem miješanjem na karakteristike zavarenog spoja kovanih ploča od legure aluminija EN AW 7049 AReport as inadecuate




Utjecaj kinematičkih faktora zavarivanja trenjem miješanjem na karakteristike zavarenog spoja kovanih ploča od legure aluminija EN AW 7049 A - Download this document for free, or read online. Document in PDF available to download.

Technical gazette, Vol.24 No.3 June 2017. -

In this paper, the influence of rotation speed and welding speed on the impact strength, microstructure and cross section micro hardness of FSW welded joints of Al-Zn-Mg-Cu high strength aluminium alloy is studied. Rotation speed was varied from 750 min−1 to 850 min−1 and welding speed from 60 mm-min to 80 mm-min. It was found that the energy of crack propagation is up to three times higher than the energy of crack initiation. This ratio was found by testing the Charpy notched specimens taken from left and right from the weld centre, 4 mm from the notch in a direction opposite to a direction of welding. Micro hardness distribution in the nugget does not show large dissipation of value regardless if the measuring point is in the upper or lower section of the nugget. Weld microstructure characteristics and zones are clearly defined at the basis of grain size and material flow.

dynamic recrystallization; friction stir welding; impact strength; micro hardness distribution



Author: Milenko Perović - orcid.org-0000-0001-6171-0215 ; Chamber of Economy of Montenegro, Novaka Miloševa 29-II, 81000 Podgorica, Mon

Source: http://hrcak.srce.hr/



DOWNLOAD PDF




Related documents