Structural effect of heavy ion irradiation on GdBaCuO ceramics - Download this document for free, or read online. Document in PDF available to download.

1 CSNSM - Centre de Spectrométrie Nucléaire et de Spectrométrie de Masse

Abstract : The influence of twin boundaries as sinks on defects induced by 480 keV Kr ion irradiation in GdBaCuO crystals was observed in situ at 40 and 300 K. The interaction of the dislocations with the twin boundaries followed on a video recording. A crystalline to amorphous transition was observed above a total fluence of ∼ 4 - 5 x 10^12 Kr-cm2. A comparison between orthorhombic Os crystals and a monoclinic structure Ms close to Os and whose parameters were calculated shows that the behaviour of irradiation-induced extended defects does not depend on a small initial deformation of the orthorhombic cell. In both case, an occasional orthorhombic or monoclinic to tetragonal phase transition only occurs when the amorphization process has begun.

Keywords : amorphisation barium compounds dislocations gadolinium compounds high temperature superconductors ion beam effects solid state phase transformations twin boundaries Kr ions heavy ion irradiation crystalline to amorphous transition orthorhombic monoclinic tetragonal phase transition amorphization 480 keV 40 to 300 K GdBaCuO





Author: M.-O. Ruault - H. Bernas - M. Gasgnier J.-C. Levet H. Noel P. Gougeon M. Potel