Mechanical Behaviour and Fracture Mechanics of Praseodymium Modified Lead Titanate Ceramics Prepared by Solid-State Reaction RouteReport as inadecuate




Mechanical Behaviour and Fracture Mechanics of Praseodymium Modified Lead Titanate Ceramics Prepared by Solid-State Reaction Route - Download this document for free, or read online. Document in PDF available to download.

Journal of CeramicsVolume 2013 2013, Article ID 280605, 9 pages

Research ArticleCrystal Growth and Materials Research Laboratory, Department of Physics and Electronics, University of Jammu, Jammu 180006, India

Received 27 December 2012; Accepted 25 July 2013

Academic Editor: Zhenxing Yue

Copyright © 2013 Vishal Singh et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

The praseodymium modified lead titanate ceramics with composition where = 0.04, 0.06, 0.08, and 0.10 prepared by solid-state reaction technique were subjected to indentation induced hardness testing method. The indentations were induced in the applied load ranging from 0.245 N to 4.90 N. The microhardness varies nonlinearly with load and was best explained by the concept of Newtonian resistance pressure as proposed by Hays and Kendall’s law. Crack propagation, fracture toughness , brittleness index , and yield strength were studied to understand the effect of Pr content on various mechanical parameters. The load independent values were found to increase with the increase in praseodymium content.





Author: Vishal Singh, Shivani Suri, and K. K. Bamzai